Bonded Magnet and application of the magnetic properties
calendering process bonded magnets made in order to maintain its flexibility, for the general use
of powder size of the magnetic 1-1.5 ¦Ì m, by adding more of the amount of binder, most of the use of
this process ferrite magnetic particle, the thickness of the various products is the board bar, and
then re-use tool cut into other shapes. As easy to bend, can be easily manufactured multi-polar
magnetic ring, raw materials and manufacturing costs lower, uses very broad and can be used for
micro-electronics, printers clips, large billboards and children's toys, etc.. This process bonded
magnets made of the largest energy product (BH) max = 4-6.4kJ/m3 (isotropic), to improve magnetic
properties, which may be included in an adequate number of Nd-Fe-B powder was practical Bond Magnets
(BH) max = 9.6-11.2kJ/m3, with the anisotropy of bonded magnets made of the magnetic properties of
the same.
for the injection molding process, in order to guarantee the flow of magnetic intensity and
magnetic, joined more binder, therefore, the magnetic properties of bonded magnets and calendering
process of the same. Injection molding process to produce anisotropic magnets, that is injected into
the mold aggregates will certainly increase the constant magnetic field or pulse magnetic field, so
as to enhance the magnetic properties of bonded magnets. The major products for the instrumentation,
such as motor vehicles, vessels, aircraft speedometer, fuel tables and tables of current and voltage.
extrusion technology suitable for manufacturing a thin sheet of thin-walled high or high ring
bonded magnets. Binder added a calendar and the amount of injection is less than the general magnetic
properties (BH) max = 3.2-4.8kJ/m3 (isotropic), and products are mainly used in gaskets, small
advertisements and signs in the motor . Because of the restrictions and production equipment,
rolling, extrusion and injection molding process for most of ferrite powder, the magnetic properties
of products than lower. Molding is the most extensive application of a process, in particular the
rapid quenching NdFeB powder occurred, has made rapid development. Since joining binder of small, the
same type of material, molding obtained by the magnetic properties of the best magnets. Bond cobalt
iron boron permanent magnet almost all use of fast quenching powder as raw materials (with a small
magnetic particle production HDDR process), basically a molding process, the magnetic properties of
the highest. (BH) max = 64-96kJ/m3 (isotropic), the application market is very extensive.
of powder size of the magnetic 1-1.5 ¦Ì m, by adding more of the amount of binder, most of the use of
this process ferrite magnetic particle, the thickness of the various products is the board bar, and
then re-use tool cut into other shapes. As easy to bend, can be easily manufactured multi-polar
magnetic ring, raw materials and manufacturing costs lower, uses very broad and can be used for
micro-electronics, printers clips, large billboards and children's toys, etc.. This process bonded
magnets made of the largest energy product (BH) max = 4-6.4kJ/m3 (isotropic), to improve magnetic
properties, which may be included in an adequate number of Nd-Fe-B powder was practical Bond Magnets
(BH) max = 9.6-11.2kJ/m3, with the anisotropy of bonded magnets made of the magnetic properties of
the same.
for the injection molding process, in order to guarantee the flow of magnetic intensity and
magnetic, joined more binder, therefore, the magnetic properties of bonded magnets and calendering
process of the same. Injection molding process to produce anisotropic magnets, that is injected into
the mold aggregates will certainly increase the constant magnetic field or pulse magnetic field, so
as to enhance the magnetic properties of bonded magnets. The major products for the instrumentation,
such as motor vehicles, vessels, aircraft speedometer, fuel tables and tables of current and voltage.
extrusion technology suitable for manufacturing a thin sheet of thin-walled high or high ring
bonded magnets. Binder added a calendar and the amount of injection is less than the general magnetic
properties (BH) max = 3.2-4.8kJ/m3 (isotropic), and products are mainly used in gaskets, small
advertisements and signs in the motor . Because of the restrictions and production equipment,
rolling, extrusion and injection molding process for most of ferrite powder, the magnetic properties
of products than lower. Molding is the most extensive application of a process, in particular the
rapid quenching NdFeB powder occurred, has made rapid development. Since joining binder of small, the
same type of material, molding obtained by the magnetic properties of the best magnets. Bond cobalt
iron boron permanent magnet almost all use of fast quenching powder as raw materials (with a small
magnetic particle production HDDR process), basically a molding process, the magnetic properties of
the highest. (BH) max = 64-96kJ/m3 (isotropic), the application market is very extensive.